INVESTIGATION OF SCREWS FOUND IN WILHELM ORE MINE
|
|
- Wacław Urbaniak
- 7 lat temu
- Przeglądów:
Transkrypt
1 Key words: cast steel, puddled steel, ore mine, steel screw Andrzej ŻAK * INVESTIGATION OF SCREWS FOUND IN WILHELM ORE MINE This article presents macro- and microscopic investigation of steel screws which were found during exploration ore mine Wilhelm. The mine is placed in Lower Silesia and was closed in year During investigation I proved that they were produced of puddled or cast steel. It has been confirmed, that screws were made at the turn on 19 th and 20 th century. I also described differences in heat treatment between two objects. 1. INTRODUCTION 1.1. ORIGIN OF THE ISSUE In the year 2011, during exploration of closed ore mine Wilhelm in Lower Silesia some old steel screw were found. Mine worked from year 1897 to It was necessary to find out if screws were really produced at the turn on 19 th and 20 th century or they were left there later. Investigation were done in laboratories of Institute of Materials Science and Applied Mechanics EXAMINATED OBJECTS Screws were covered with rust and other products of corrosion process (fig.1). They were put into container with rust remover for about twelve hours. Some products of corrosion were also mechanically removed. As a result there were obtained a quite pure surface of both objects (fig.2). * Wroclaw University of Technology, Faculty of Mechanics, I. Łukasiewicza 5, Wrocław
2 Fig. 1. Screws before preparing.. Fig. 2. Screws after preparing. 2. MACROSTRUCTURES AND MICROSTRUCTURES OF SCREWS 2.1. MACROSTRUCTURE Screws were cut, polished and etched (fig.3). In the bigger screw we can clearly see effects of forging the material. It has been cold worked at temperature below its recrystallization temperature. There is also visible a great amount of corrosion effects. Screw was for sure not heat treated. We can see a lot of non-metallic impurities. Smaller screw is also corroded, especially at a bolt head. In the cylindrical part we can see some signs of plastic deformation at temperature below recrystallization temperature. Very interesting is a structure of a bolt head. It had been heat treated in the end of production process. Structure is characteristic for steel after normalization. The head were probably heated above the upper critical temperature and then cooled in open air.
3 Fig. 3. Macrostructure of the bigger and smaller screw MICROSTRUCTURE Microscopic views of the bigger screw structure (fig.4, fig.5) show the structure characteristic to old puddled steel [1][4]. There are a lot of big, non-metallic impurities (fig.4). They have significantly decreased strength of material. In greater magnification (fig.5) we can see a structure composed of ferrite and small amount of cementite at the grain boundaries. It is one of the effects of microstructural degradation processes. Another visible effects are small, non-metallic impurities both inside the grains and at the grain boundaries. Amount of carbon in analyzed alloy is low, material is probably made by iron, silicon, manganese, sulfur and phosphorus [1]. Microscopic structure is similar to structure of steel from Pomorski Środkowy Bridge in Wroclaw, presented in Grzegorz Lesiuk and Mieczysław Szata article [4]. Microscopic views of the smaller screw structure (fig.6, fig.7) show the structure characteristic to the old cast steel [1][4][5]. It is hypo-eutectoid composed of ferrite and lamellar pearlite. In the cylindrical body structure is banded to direction of plastic deformation (fig. 6). Amount of carbon is greater than in the bigger screw and the amount of on-metallic impurities is a few times smaller. There are also some signs of microstructural degradation process. In bands of ferrite there are few impurities in the middle of grains and cementite at the grain boundaries (fig. 7). Also pearlite was locally separated into ferrite and cementite. It is one of the greater signs of degradation
4 process [5]. Microstructure is similar to the view of steel from Pomorski Północny Bridge in Wroclaw [4]. Fig. 4. Microstructure of the bigger screw magnification 100x. Fig. 5. Microstructure of the bigger screw magnification 400x.
5 Fig. 6. Microstructure of the smaller screw magnification 100x. Fig. 7. Microstructure of the smaller screw magnification 400x.
6 3. SUMMARY Two screws found in the Wilhelm ore mine have completely different structure. The biggest one was produced from puddle steel typical to a second half of 19 th century. The smallest screw was produced from the modern cast steel. It was also heat treated in a selected part for better strength. Objects were found in the level of 120 meters depth [10], active in years It was confirmed that bigger screw was produced at the turn on 19 th and 20 th century. The second one probably was produced in early 20 th century. REFERENCES [1]CZAPLIŃSKI Kazimierz, Dawne wyroby ze stopów żelaza, Wydawnictwo DWE, Wrocław 2009; [2]DUDZIŃSKI Włodzimierz, WIDANKA Krzysztof, Ćwiczenia laboratoryjne z materiałoznawstwa, Oficyna Wydawnicza Politechniki Wrocławskiej, Wrocław 2009; [3]HAIMANN Rudolf, Metaloznawstwo, Politechnika Wrocławska, Wrocław 1980; [4]LESIUK Grzegorz, SZATA Mieczysław, Degradacja mikrostruktur elementów konstrukcyjnych pochodzących z mostów wzniesionych na przełomie XIX i XX wieku, in: Zeszyty naukowe WSOWL, 1/2010; [5]PĘKALSKI Grzegorz, Degradacja maszyn wydobywczych zagadnienia materiałowe, IMiMTPWr, Wrocław; [6]PĘKALSKI Grzegorz, Korozja i ochrona przeciwkorozyjna, IMiMTPWr, Wrocław 1987/88; [7]PIECHOTA Stanisław, Technika podziemnej eksploatacji rud, Wydawnictwo AGH, Kraków 1988; [8]PŁANETA Stefan, Systemy eksploatacji podziemnej złóż rud. Koncepcja i praktyka górnicza, Oficyna Wydawnicza Politechniki Wrocławskiej, Wrocław 2009; [9]SADOWSKI Roman, Do Radzimowic po złoto i?, in: bolkow.net; [10]Kopalnia Stara Góra. Plan robót górniczych. Sekcja 9, Przedsiębiorstwo Geologiczne Rud Nieżelaznych z tymczasową siedzibą w Stalinogrodzie, , archiwum prywatne Adam Wojcieszonek;. BADANIE ŚRUB ZNALEZIONYCH W NIECZYNNEJ KOPALNI RUD METALI WILHELM Artykuł prezentuje badania makro- i mikrostruktury śrub stalowych znalezionych podczas eksploracji zamkniętej w roku 1925 kopalni Wilhelm na Dolnym Śląsku. Na drodze analizy zgładów metalograficznych wyróżniono struktury charakterystyczne dla starych stali zgrzewnych i zlewnych. Potwierdzono tym samym wiek elementów na przełom XIX i XX wieku. Dostrzeżono ponadto ślady bardzo starannej obróbki cieplnej na jednym z obiektów, wykonanym ze stali zlewnej. Zasygnalizowało to wysoki poziom wiedzy i staranności u producenta tego elementu.
SSW1.1, HFW Fry #20, Zeno #25 Benchmark: Qtr.1. Fry #65, Zeno #67. like
SSW1.1, HFW Fry #20, Zeno #25 Benchmark: Qtr.1 I SSW1.1, HFW Fry #65, Zeno #67 Benchmark: Qtr.1 like SSW1.2, HFW Fry #47, Zeno #59 Benchmark: Qtr.1 do SSW1.2, HFW Fry #5, Zeno #4 Benchmark: Qtr.1 to SSW1.2,
Bardziej szczegółowoKonsorcjum Śląskich Uczelni Publicznych
Konsorcjum Śląskich Uczelni Publicznych Dlaczego powstało? - świat przeżywa dziś rewolucję w obszarze edukacji, - naszym celem jest promocja śląskiego jako regionu opartego na wiedzy, i najnowszych technologiach,
Bardziej szczegółowoCracow University of Economics Poland. Overview. Sources of Real GDP per Capita Growth: Polish Regional-Macroeconomic Dimensions 2000-2005
Cracow University of Economics Sources of Real GDP per Capita Growth: Polish Regional-Macroeconomic Dimensions 2000-2005 - Key Note Speech - Presented by: Dr. David Clowes The Growth Research Unit CE Europe
Bardziej szczegółowoWydział Fizyki, Astronomii i Informatyki Stosowanej Uniwersytet Mikołaja Kopernika w Toruniu
IONS-14 / OPTO Meeting For Young Researchers 2013 Khet Tournament On 3-6 July 2013 at the Faculty of Physics, Astronomy and Informatics of Nicolaus Copernicus University in Torun (Poland) there were two
Bardziej szczegółowoTYRE PYROLYSIS. REDUXCO GENERAL DISTRIBUTOR :: ::
TYRE PYROLYSIS Installation for rubber waste pyrolysis designed for processing of used tyres and plastic waste (polyethylene, polypropylene, polystyrene), where the final product could be electricity,
Bardziej szczegółowowww.irs.gov/form990. If "Yes," complete Schedule A Schedule B, Schedule of Contributors If "Yes," complete Schedule C, Part I If "Yes," complete Schedule C, Part II If "Yes," complete Schedule C, Part
Bardziej szczegółowophoto graphic Jan Witkowski Project for exhibition compositions typography colors : +48 506 780 943 : janwi@janwi.com
Jan Witkowski : +48 506 780 943 : janwi@janwi.com Project for exhibition photo graphic compositions typography colors Berlin London Paris Barcelona Vienna Prague Krakow Zakopane Jan Witkowski ARTIST FROM
Bardziej szczegółowoDOI: / /32/37
. 2015. 4 (32) 1:18 DOI: 10.17223/1998863 /32/37 -,,. - -. :,,,,., -, -.,.-.,.,.,. -., -,.,,., -, 70 80. (.,.,. ),, -,.,, -,, (1886 1980).,.,, (.,.,..), -, -,,,, ; -, - 346, -,.. :, -, -,,,,,.,,, -,,,
Bardziej szczegółowoINSPECTION METHODS FOR QUALITY CONTROL OF FIBRE METAL LAMINATES IN AEROSPACE COMPONENTS
Kompozyty 11: 2 (2011) 130-135 Krzysztof Dragan 1 * Jarosław Bieniaś 2, Michał Sałaciński 1, Piotr Synaszko 1 1 Air Force Institute of Technology, Non Destructive Testing Lab., ul. ks. Bolesława 6, 01-494
Bardziej szczegółowoHas the heat wave frequency or intensity changed in Poland since 1950?
Has the heat wave frequency or intensity changed in Poland since 1950? Joanna Wibig Department of Meteorology and Climatology, University of Lodz, Poland OUTLINE: Motivation Data Heat wave frequency measures
Bardziej szczegółowowww.irs.gov/form990. If "Yes," complete Schedule A Schedule B, Schedule of Contributors If "Yes," complete Schedule C, Part I If "Yes," complete Schedule C, Part II If "Yes," complete Schedule C, Part
Bardziej szczegółowoWojewodztwo Koszalinskie: Obiekty i walory krajoznawcze (Inwentaryzacja krajoznawcza Polski) (Polish Edition)
Wojewodztwo Koszalinskie: Obiekty i walory krajoznawcze (Inwentaryzacja krajoznawcza Polski) (Polish Edition) Robert Respondowski Click here if your download doesn"t start automatically Wojewodztwo Koszalinskie:
Bardziej szczegółowoZakopane, plan miasta: Skala ok. 1: = City map (Polish Edition)
Zakopane, plan miasta: Skala ok. 1:15 000 = City map (Polish Edition) Click here if your download doesn"t start automatically Zakopane, plan miasta: Skala ok. 1:15 000 = City map (Polish Edition) Zakopane,
Bardziej szczegółowoStruktury proponowane dla unikalnych rozwiązań architektonicznych.
23 Struktury proponowane dla unikalnych rozwiązań architektonicznych.. System fundamentu zespolonego może być zastosowany jako bezpieczna podstawa dla obiektów silnie obciążonych mogących być zlokalizowanymi
Bardziej szczegółowoDO MONTAŻU POTRZEBNE SĄ DWIE OSOBY! INSTALLATION REQUIRES TWO PEOPLE!
1 HAPPY ANIMALS B09 INSTRUKCJA MONTAŻU ASSEMBLY INSTRUCTIONS Akcesoria / Fittings K1 M M1 ZM1 Z T G1 17 szt. / pcs 13 szt. / pcs B1 13 szt. / pcs W4 13 szt. / pcs W6 14 szt. / pcs U1 1 szt. / pcs U N1
Bardziej szczegółowoERASMUS + : Trail of extinct and active volcanoes, earthquakes through Europe. SURVEY TO STUDENTS.
ERASMUS + : Trail of extinct and active volcanoes, earthquakes through Europe. SURVEY TO STUDENTS. Strona 1 1. Please give one answer. I am: Students involved in project 69% 18 Student not involved in
Bardziej szczegółowoPatients price acceptance SELECTED FINDINGS
Patients price acceptance SELECTED FINDINGS October 2015 Summary With growing economy and Poles benefiting from this growth, perception of prices changes - this is also true for pharmaceuticals It may
Bardziej szczegółowoXT001_ INTRODUCTION TO EXIT INTERVIEW PYTANIE NIE JEST ZADAWANE W POLSCE W 2006 ROKU. WCIŚNIJ Ctrl+R BY PRZEJŚĆ DALEJ. 1.
Share w2 Exit Questionnaire version 2.7 2006-09-29 XT001_ INTRODUCTION TO EXIT INTERVIEW 1. Kontynuuj XT006_ PROXY RESPONDENT'S SEX 1. Mężczyzna 2. Kobieta XT002_ RELATIONSHIP TO THE DECEASED IF XT002_
Bardziej szczegółowoStargard Szczecinski i okolice (Polish Edition)
Stargard Szczecinski i okolice (Polish Edition) Janusz Leszek Jurkiewicz Click here if your download doesn"t start automatically Stargard Szczecinski i okolice (Polish Edition) Janusz Leszek Jurkiewicz
Bardziej szczegółowoIDENTYFIKACJA FAZ W MODYFIKOWANYCH CYRKONEM ŻAROWYTRZYMAŁYCH ODLEWNICZYCH STOPACH KOBALTU METODĄ DEBYEA-SCHERRERA
44/14 Archives of Foundry, Year 2004, Volume 4, 14 Archiwum Odlewnictwa, Rok 2004, Rocznik 4, Nr 14 PAN Katowice PL ISSN 1642-5308 IDENTYFIKACJA FAZ W MODYFIKOWANYCH CYRKONEM ŻAROWYTRZYMAŁYCH ODLEWNICZYCH
Bardziej szczegółowoETNA BOXES DO KABIN PRYSZNICOWYCH SHOWER. Zawiasy i klamry do kabin prysznicowych Shower hinges and clamps AKCESORIA ACCESSORIES
Zawiasy i klamry do kabin prysznicowych Shower hinges and clamps AKCESORIA DO KABIN PRYSZNICOWYCH SHOWER BOXES ACCESSORIES ZAWIASY I KLAMRY DO KABIN PRYSZNICOWYCH SHOWER HINGES AND CLAMPS TGHU - ZAWIASY
Bardziej szczegółowoPielgrzymka do Ojczyzny: Przemowienia i homilie Ojca Swietego Jana Pawla II (Jan Pawel II-- pierwszy Polak na Stolicy Piotrowej) (Polish Edition)
Pielgrzymka do Ojczyzny: Przemowienia i homilie Ojca Swietego Jana Pawla II (Jan Pawel II-- pierwszy Polak na Stolicy Piotrowej) (Polish Edition) Click here if your download doesn"t start automatically
Bardziej szczegółowo2 nd ClimMani EU COST Action Meeting Poznań, Poland 28-30 September, 2015
nd ClimMani EU COST Action Meeting, oland 8-30 September, 015 Venue HOTEL MERCURE**** - OZNAŃ Address: ul. Roosvelta 0, 60-89, oland Tel. +48 61 855 80 00 e-mail: H3393@accor.com mercure-poznan-centrum.com
Bardziej szczegółowoKONTROLA STALIWA NIESTOPOWEGO METODĄ ATD
36/12 ARCHIWUM ODLEWNICTWA Rok 2004, Rocznik 4, Nr 12 Archives of Foundry Year 2004, Volume 4, Book 12 PAN Katowice PL ISSN 1642-5308 KONTROLA STALIWA NIESTOPOWEGO METODĄ ATD S. PIETROWSKI 1, G. GUMIENNY
Bardziej szczegółowoSPITSBERGEN HORNSUND
Polska Stacja Polarna Instytut Geofizyki Polska Akademia Nauk Polish Polar Station Institute of Geophysics Polish Academy of Sciences BIULETYN METEOROLOGICZNY METEOROLOGICAL BULLETIN SPITSBERGEN HORNSUND
Bardziej szczegółowoJęzyk angielski. Gry i zabawy. Podróże dalekie i bliskie
Język angielski Gry i zabawy Podróże dalekie i bliskie Tytuł oryginału: 365 gier i zabaw dla całej rodziny. Język angielski Autorzy oryginału: Natalia Kertyczak, Ewa Mikołajska, Radosław Mikołajski, Małgorzata
Bardziej szczegółowoSargent Opens Sonairte Farmers' Market
Sargent Opens Sonairte Farmers' Market 31 March, 2008 1V8VIZSV7EVKIRX8(1MRMWXIVSJ7XEXIEXXLI(ITEVXQIRXSJ%KVMGYPXYVI *MWLIVMIWERH*SSHTIVJSVQIHXLISJJMGMEPSTIRMRKSJXLI7SREMVXI*EVQIVW 1EVOIXMR0E]XS[R'S1IEXL
Bardziej szczegółowoProjekty Marie Curie Actions w praktyce: EGALITE (IAPP) i ArSInformatiCa (IOF)
Gliwice, Poland, 28th February 2014 Projekty Marie Curie Actions w praktyce: EGALITE (IAPP) i ArSInformatiCa (IOF) Krzysztof A. Cyran The project has received Community research funding under the 7th Framework
Bardziej szczegółowoKrytyczne czynniki sukcesu w zarządzaniu projektami
Seweryn SPAŁEK Krytyczne czynniki sukcesu w zarządzaniu projektami MONOGRAFIA Wydawnictwo Politechniki Śląskiej Gliwice 2004 SPIS TREŚCI WPROWADZENIE 5 1. ZARZĄDZANIE PROJEKTAMI W ORGANIZACJI 13 1.1. Zarządzanie
Bardziej szczegółowoTest sprawdzający znajomość języka angielskiego
Test sprawdzający znajomość języka angielskiego Imię i Nazwisko Kandydata/Kandydatki Proszę wstawić X w pole zgodnie z prawdą: Brak znajomości języka angielskiego Znam j. angielski (Proszę wypełnić poniższy
Bardziej szczegółowoOBRÓBKA CIEPLNA STOPOWYCH KOMPOZYTÓW POWIERZCHNIOWYCH
1/22 Archives of Foundry, Year 2006, Volume 6, 22 Archiwum Odlewnictwa, Rok 2006, Rocznik 6, Nr 22 PAN Katowice PL ISSN 1642-5308 OBRÓBKA CIEPLNA STOPOWYCH KOMPOZYTÓW POWIERZCHNIOWYCH C. BARON 1, J. GAWROŃSKI
Bardziej szczegółowoCracow University of Economics Poland
Cracow University of Economics Poland Sources of Real GDP per Capita Growth: Polish Regional-Macroeconomic Dimensions 2000-2005 - Keynote Speech - Presented by: Dr. David Clowes The Growth Research Unit,
Bardziej szczegółowoA R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume Issue 4
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 54 2009 Issue 4 D. LEŚNIAK STRUCTURE AND MECHANICAL PROPERTIES OF EXTRUDED AlCuMg SECTIONS IN T5 TEMPER STRUKTURA I WŁASNOŚCI MECHANICZNE
Bardziej szczegółowoFILTRACJA STOPU AlSi9Mg (AK9) M. DUDYK 1 Wydział Budowy Maszyn i Informatyki Akademia Techniczno - Humanistyczna ul. Willowa 2, Bielsko-Biała.
8/17 ARCHIWUM ODLEWNICTWA Rok 2005, Rocznik 5, Nr 17 Archives of Foundry Year 2005, Volume 5, Book 17 PAN - Katowice PL ISSN 1642-5308 FILTRACJA STOPU AlSi9Mg (AK9) M. DUDYK 1 Wydział Budowy Maszyn i Informatyki
Bardziej szczegółowoRobotic Arm Assembly Manual
Robotic Arm Assembly Manual 1. List of materials 3D printed Parts: Part Quantity Arm 1 gear.stl 1 Arm 1 lower.stl 1 Arm 1 upper.stl 1 Arm 2.STL 1 Arm 3.STL 1 Base gear.stl 1 Base.STL 1 Grasper 1.STL 1
Bardziej szczegółowoKONTROLA STALIWA GXCrNi72-32 METODĄ ATD
54/14 Archives of Foundry, Year 2004, Volume 4, 14 Archiwum Odlewnictwa, Rok 2004, Rocznik 4, Nr 14 PAN Katowice PL ISSN 1642-5308 KONTROLA STALIWA GXCrNi72-32 METODĄ ATD S. PIETROWSKI 1, G. GUMIENNY 2
Bardziej szczegółowoSPITSBERGEN HORNSUND
Polska Stacja Polarna Instytut Geofizyki Polska Akademia Nauk Polish Polar Station Institute of Geophysics Polish Academy of Sciences BIULETYN METEOROLOGICZNY METEOROLOGICAL BULLETIN SPITSBERGEN HORNSUND
Bardziej szczegółowoEmilka szuka swojej gwiazdy / Emily Climbs (Emily, #2)
Emilka szuka swojej gwiazdy / Emily Climbs (Emily, #2) Click here if your download doesn"t start automatically Emilka szuka swojej gwiazdy / Emily Climbs (Emily, #2) Emilka szuka swojej gwiazdy / Emily
Bardziej szczegółowoUszczelnianie profili firmy KLUŚ na przykładzie profilu PDS 4 - ALU / Sealing KLUŚ profiles on example of PDS 4 - ALU profile. Pasek LED / LED strip
Uszczelnianie profili firmy KLUŚ na przykładzie profilu PDS 4 - ALU / Sealing KLUŚ profiles on example of PDS 4 - ALU profile. 1. Pasek LED / LED strip Rękaw termokurczliwy / heat shrink sleeve Istnieje
Bardziej szczegółowoExtraclass. Football Men. Season 2009/10 - Autumn round
Extraclass Football Men Season 2009/10 - Autumn round Invitation Dear All, On the date of 29th July starts the new season of Polish Extraclass. There will be live coverage form all the matches on Canal+
Bardziej szczegółowoMaPlan Sp. z O.O. Click here if your download doesn"t start automatically
Mierzeja Wislana, mapa turystyczna 1:50 000: Mikoszewo, Jantar, Stegna, Sztutowo, Katy Rybackie, Przebrno, Krynica Morska, Piaski, Frombork =... = Carte touristique (Polish Edition) MaPlan Sp. z O.O Click
Bardziej szczegółowoOBRÓBKA CIEPLNA SILUMINU AK132
52/22 Archives of Foundry, Year 2006, Volume 6, 22 Archiwum Odlewnictwa, Rok 2006, Rocznik 6, Nr 22 PAN Katowice PL ISSN 1642-5308 OBRÓBKA CIEPLNA SILUMINU AK132 J. PEZDA 1 Akademia Techniczno-Humanistyczna
Bardziej szczegółowoBADANIA WYTRZYMA OŒCI NA ŒCISKANIE PRÓBEK Z TWORZYWA ABS DRUKOWANYCH W TECHNOLOGII FDM
dr in. Marek GOŒCIAÑSKI, dr in. Bart³omiej DUDZIAK Przemys³owy Instytut Maszyn Rolniczych, Poznañ e-mail: office@pimr.poznan.pl BADANIA WYTRZYMA OŒCI NA ŒCISKANIE PRÓBEK Z TWORZYWA ABS DRUKOWANYCH W TECHNOLOGII
Bardziej szczegółowoMachine Learning for Data Science (CS4786) Lecture 11. Spectral Embedding + Clustering
Machine Learning for Data Science (CS4786) Lecture 11 Spectral Embedding + Clustering MOTIVATING EXAMPLE What can you say from this network? MOTIVATING EXAMPLE How about now? THOUGHT EXPERIMENT For each
Bardziej szczegółowoZwora Yale US06. Yale seria US kg. Zastosowanie. Właściwości. Parametry techniczne
Zwora Yale US06 Yale seria US06 270 kg Zastosowanie Zwory serii US06 przeznaczone są do realizowania kontroli dostępu w pomieszczeniach wymagających podstawowej ochrony np. drzwi wewnętrzne. Właściwości
Bardziej szczegółowoZajęcia z języka angielskiego TELC Gimnazjum Scenariusz lekcji Prowadzący: Jarosław Gołębiewski Temat: Czas Present Perfect - wprowadzenie
Zajęcia z języka angielskiego TELC Gimnazjum Scenariusz lekcji Prowadzący: Jarosław Gołębiewski Temat: Czas Present Perfect - wprowadzenie I. Cele lekcji 1) Wiadomości Uczeń: wie, że czas present perfect
Bardziej szczegółowoBARIERA ANTYKONDENSACYJNA
Skład Obróbka Parametry techniczne BARIERA ANTYKONDENSACYJNA Lama "Lama" sp. z o.o. sp. k Właściwość Metoda badania Wartość Jednostka włóknina poliestrowa + klej PSA + folia polietylenowa Samoprzylepna
Bardziej szczegółowoWarszawa, Śródmieście, Emilii Plater Penthouse PLN PLN / m²
NA SPRZEDAŻ Warszawa, Śródmieście, Emilii Plater Penthouse 2 900 000 PLN 26 364 PLN / m² POWIERZCHNIA: 110 M² LICZBA POKOI: 3 LICZBA SYPIALNI: 2 PIĘTRO: 7/7 ROK BUDOWY: 2009 NUMER OFERTY: 21037 Opis Ekskluzywny
Bardziej szczegółowo!850016! www.irs.gov/form8879eo. e-file www.irs.gov/form990. If "Yes," complete Schedule A Schedule B, Schedule of Contributors If "Yes," complete Schedule C, Part I If "Yes," complete Schedule C,
Bardziej szczegółowoFew-fermion thermometry
Few-fermion thermometry Phys. Rev. A 97, 063619 (2018) Tomasz Sowiński Institute of Physics of the Polish Academy of Sciences Co-authors: Marcin Płodzień Rafał Demkowicz-Dobrzański FEW-BODY PROBLEMS FewBody.ifpan.edu.pl
Bardziej szczegółowoHAPPY ANIMALS L01 HAPPY ANIMALS L03 HAPPY ANIMALS L05 HAPPY ANIMALS L07
HAPPY ANIMALS L0 HAPPY ANIMALS L0 HAPPY ANIMALS L0 HAPPY ANIMALS L07 INSTRUKCJA MONTAŻU ASSEMBLY INSTRUCTIONS Akcesoria / Fittings K ZW W8 W7 Ø x 6 szt. / pcs Ø7 x 70 Narzędzia / Tools DO MONTAŻU POTRZEBNE
Bardziej szczegółowoHAPPY ANIMALS L02 HAPPY ANIMALS L04 HAPPY ANIMALS L06 HAPPY ANIMALS L08
HAPPY ANIMALS L02 HAPPY ANIMALS L04 HAPPY ANIMALS L06 HAPPY ANIMALS L08 INSTRUKCJA MONTAŻU ASSEMBLY INSTRUCTIONS Akcesoria / Fittings K O G ZW W8 W4 20 szt. / pcs 4 szt. / pcs 4 szt. / pcs 4 szt. / pcs
Bardziej szczegółowoWPŁYW PROCESU TARCIA NA ZMIANĘ MIKROTWARDOŚCI WARSTWY WIERZCHNIEJ MATERIAŁÓW POLIMEROWYCH
WOJCIECH WIELEBA WPŁYW PROCESU TARCIA NA ZMIANĘ MIKROTWARDOŚCI WARSTWY WIERZCHNIEJ MATERIAŁÓW POLIMEROWYCH THE INFLUENCE OF FRICTION PROCESS FOR CHANGE OF MICROHARDNESS OF SURFACE LAYER IN POLYMERIC MATERIALS
Bardziej szczegółowowww.irs.gov/form990. If "Yes," complete Schedule A Schedule B, Schedule of Contributors If "Yes," complete Schedule C, Part I If "Yes," complete Schedule C, Part II If "Yes," complete Schedule C, Part
Bardziej szczegółowoFor choosen profiles, KLUS company offers end caps with holes for leading power supply cable. It is also possible to drill the end cap independently
Uszczelnianie profili firmy KLUŚ na przykładzie profilu PDS 4 - ALU / Sealing KLUŚ profiles on example of PDS 4 - ALU profile. 1. Pasek LED / LED strip Rękaw termokurczliwy / heat shrink sleeve Istnieje
Bardziej szczegółowoWPŁYW WANADU I MOLIBDENU ORAZ OBRÓBKI CIEPLNEJ STALIWA Mn-Ni DLA UZYSKANIA GRANICY PLASTYCZNOŚCI POWYŻEJ 850 MPa
7/8 ARCHIWUM ODLEWNICTWA Rok 2003, Rocznik 3, Nr 8 Archives of Foundry Year 2003, Volume 3, Book 8 PAN - Katowice PL ISSN 1642-5308 WPŁYW WANADU I MOLIBDENU ORAZ OBRÓBKI CIEPLNEJ STALIWA Mn-Ni DLA UZYSKANIA
Bardziej szczegółowoKarpacz, plan miasta 1:10 000: Panorama Karkonoszy, mapa szlakow turystycznych (Polish Edition)
Karpacz, plan miasta 1:10 000: Panorama Karkonoszy, mapa szlakow turystycznych (Polish Edition) J Krupski Click here if your download doesn"t start automatically Karpacz, plan miasta 1:10 000: Panorama
Bardziej szczegółowoPRESENT TENSES IN ENGLISH by
PRESENT TENSES IN ENGLISH by Present Tenses Present Continuous Zastosowanie Czasu Present Continuous używamy, gdy mówimy: o czynności, którą wykonujemy w momencie mówienia, o czynności, w trakcie wykonywania
Bardziej szczegółowoOdpowiedzi do zadań zamieszczonych w arkuszu egzaminu ósmoklasisty z języka angielskiego 17 KWIETNIA 2019 opracowane przez ekspertów Nowej Ery
Odpowiedzi do zadań zamieszczonych w arkuszu egzaminu ósmoklasisty z języka angielskiego 17 KWIETNIA 2019 opracowane przez ekspertów Nowej Ery UWAGA: W zadaniach otwartych eksperci przygotowali odpowiedzi
Bardziej szczegółowoOSTC GLOBAL TRADING CHALLENGE MANUAL
OSTC GLOBAL TRADING CHALLENGE MANUAL Wrzesień 2014 www.ostc.com/game Po zarejestrowaniu się w grze OSTC Global Trading Challenge, zaakceptowaniu oraz uzyskaniu dostępu to produktów, użytkownik gry będzie
Bardziej szczegółowoWeronika Mysliwiec, klasa 8W, rok szkolny 2018/2019
Poniższy zbiór zadań został wykonany w ramach projektu Mazowiecki program stypendialny dla uczniów szczególnie uzdolnionych - najlepsza inwestycja w człowieka w roku szkolnym 2018/2019. Tresci zadań rozwiązanych
Bardziej szczegółowoDUAL SIMILARITY OF VOLTAGE TO CURRENT AND CURRENT TO VOLTAGE TRANSFER FUNCTION OF HYBRID ACTIVE TWO- PORTS WITH CONVERSION
ELEKTRYKA 0 Zeszyt (9) Rok LX Andrzej KUKIEŁKA Politechnika Śląska w Gliwicach DUAL SIMILARITY OF VOLTAGE TO CURRENT AND CURRENT TO VOLTAGE TRANSFER FUNCTION OF HYBRID ACTIVE TWO- PORTS WITH CONVERSION
Bardziej szczegółowoDODATKOWE ĆWICZENIA EGZAMINACYJNE
I.1. X Have a nice day! Y a) Good idea b) See you soon c) The same to you I.2. X: This is my new computer. Y: Wow! Can I have a look at the Internet? X: a) Thank you b) Go ahead c) Let me try I.3. X: What
Bardziej szczegółowoBaptist Church Records
Baptist Church Records The Baptist religion was a religious minority in Poland, making it more difficult to know when and where records of this religion might be available. In an article from Rodziny,
Bardziej szczegółowoLesson 46 ZAIMKI. przymiotnik w funkcji dzierżawczej / zaimek dzierżawczy Liczba pojedyncza
Lesson 46 ZAIMKI Wersja A Opracowanie: Łukasz Aniśkiewicz Konsultacja: Bogna Ferensztajn W przeciwieństwie do angielskich rzeczowników, które zazwyczaj nie zmieniają formy z wyjątkiem końcówki "-s" w liczbie
Bardziej szczegółowoCountry fact sheet. Noise in Europe overview of policy-related data. Poland
Country fact sheet Noise in Europe 2015 overview of policy-related data Poland April 2016 The Environmental Noise Directive (END) requires EU Member States to assess exposure to noise from key transport
Bardziej szczegółowoAKCESORIA DO KABIN PRYSZNICOWYCH SHOWER ENCLOSURES FITTINGS VESUVIO
VESUVIO VESUVIO ZAWIASY I KLAMRY DO KABIN PRYSZNICOWYCH SHOWER HINGES AND CLAMPS ZAWIASY UNOSZONE TTU LIFTED HINGES TTU TTU90LH TTU90RH TTU90-OSLH TTU90-OSRH TTU10LH TTU10RH TTU90GGLH TTU90GGRH KLAMRY
Bardziej szczegółowoZGŁOSZENIE WSPÓLNEGO POLSKO -. PROJEKTU NA LATA: APPLICATION FOR A JOINT POLISH -... PROJECT FOR THE YEARS:.
ZGŁOSZENIE WSPÓLNEGO POLSKO -. PROJEKTU NA LATA: APPLICATION FOR A JOINT POLISH -... PROJECT FOR THE YEARS:. W RAMACH POROZUMIENIA O WSPÓŁPRACY NAUKOWEJ MIĘDZY POLSKĄ AKADEMIĄ NAUK I... UNDER THE AGREEMENT
Bardziej szczegółowoMachine Learning for Data Science (CS4786) Lecture11. Random Projections & Canonical Correlation Analysis
Machine Learning for Data Science (CS4786) Lecture11 5 Random Projections & Canonical Correlation Analysis The Tall, THE FAT AND THE UGLY n X d The Tall, THE FAT AND THE UGLY d X > n X d n = n d d The
Bardziej szczegółowoFig 5 Spectrograms of the original signal (top) extracted shaft-related GAD components (middle) and
Fig 4 Measured vibration signal (top). Blue original signal. Red component related to periodic excitation of resonances and noise. Green component related. Rotational speed profile used for experiment
Bardziej szczegółowoJak zasada Pareto może pomóc Ci w nauce języków obcych?
Jak zasada Pareto może pomóc Ci w nauce języków obcych? Artykuł pobrano ze strony eioba.pl Pokazuje, jak zastosowanie zasady Pareto może usprawnić Twoją naukę angielskiego. Słynna zasada Pareto mówi o
Bardziej szczegółowoNetwork Services for Spatial Data in European Geo-Portals and their Compliance with ISO and OGC Standards
INSPIRE Conference 2010 INSPIRE as a Framework for Cooperation Network Services for Spatial Data in European Geo-Portals and their Compliance with ISO and OGC Standards Elżbieta Bielecka Agnieszka Zwirowicz
Bardziej szczegółowoWojewodztwo Koszalinskie: Obiekty i walory krajoznawcze (Inwentaryzacja krajoznawcza Polski) (Polish Edition)
Wojewodztwo Koszalinskie: Obiekty i walory krajoznawcze (Inwentaryzacja krajoznawcza Polski) (Polish Edition) Robert Respondowski Click here if your download doesn"t start automatically Wojewodztwo Koszalinskie:
Bardziej szczegółowoWYKAZ PRÓB / SUMMARY OF TESTS
Strona/Page 2/9 WYKAZ PRÓB / SUMMARY OF TESTS PN-EN 61643-11:2006 STRONA PAGE Próba nieusuwalności znakowania Test of indelibility of markings Próba niezawodności śrub, części przewodzących i połączeń
Bardziej szczegółowoKatowice, plan miasta: Skala 1: = City map = Stadtplan (Polish Edition)
Katowice, plan miasta: Skala 1:20 000 = City map = Stadtplan (Polish Edition) Polskie Przedsiebiorstwo Wydawnictw Kartograficznych im. Eugeniusza Romera Click here if your download doesn"t start automatically
Bardziej szczegółowoWPŁYW CHROPOWATOŚCI POWIERZCHNI MATERIAŁU NA GRUBOŚĆ POWŁOKI PO ALFINOWANIU
51/17 ARCHIWUM ODLEWNICTWA Rok 2005, Rocznik 5, Nr 17 Archives of Foundry Year 2005, Volume 5, Book 17 PAN - Katowice PL ISSN 1642-5308 WPŁYW CHROPOWATOŚCI POWIERZCHNI MATERIAŁU NA GRUBOŚĆ POWŁOKI PO ALFINOWANIU
Bardziej szczegółowoStrategic planning. Jolanta Żyśko University of Physical Education in Warsaw
Strategic planning Jolanta Żyśko University of Physical Education in Warsaw 7S Formula Strategy 5 Ps Strategy as plan Strategy as ploy Strategy as pattern Strategy as position Strategy as perspective Strategy
Bardziej szczegółowoWykaz linii kolejowych, które są wyposażone w urządzenia systemu ETCS
Wykaz kolejowych, które są wyposażone w urządzenia W tablicy znajdującej się na kolejnych stronach tego załącznika zastosowano następujące oznaczenia: - numer kolejowej według instrukcji Wykaz Id-12 (D-29).
Bardziej szczegółowoWPŁYW ALUMINIUM NA NIEKTÓRE WŁAŚCIWOŚCI I STRUKTURĘ STALIWA
23/15 Archives of Foundry, Year 2005, Volume 5, 15 Archiwum Odlewnictwa, Rok 2005, Rocznik 5, Nr 15 PAN Katowice PL ISSN 1642-5308 WPŁYW ALUMINIUM NA NIEKTÓRE WŁAŚCIWOŚCI I STRUKTURĘ STALIWA J. KILARSKI
Bardziej szczegółowoMODYFIKACJA STOPU AK64
17/10 Archives of Foundry, Year 2003, Volume 3, 10 Archiwum Odlewnictwa, Rok 2003, Rocznik 3, Nr 10 PAN Katowice PL ISSN 1642-5308 MODYFIKACJA STOPU AK64 F. ROMANKIEWICZ 1, R. ROMANKIEWICZ 2, T. PODRÁBSKÝ
Bardziej szczegółowoEXAMPLES OF CABRI GEOMETRE II APPLICATION IN GEOMETRIC SCIENTIFIC RESEARCH
Anna BŁACH Centre of Geometry and Engineering Graphics Silesian University of Technology in Gliwice EXAMPLES OF CABRI GEOMETRE II APPLICATION IN GEOMETRIC SCIENTIFIC RESEARCH Introduction Computer techniques
Bardziej szczegółowoNOWOCZESNE ODMIANY ŻELIWA O STRUKTURZE AUSFERRYTYCZNEJ. A. KOWALSKI, A. PYTEL Instytut Odlewnictwa, ul. Zakopiańska 73, Kraków
97/18 ARCHIWUM ODLEWNICTWA Rok 2006, Rocznik 6, Nr 18 (2/2) ARCHIVES OF FOUNDRY Year 2006, Volume 6, N o 18 (2/2) PAN Katowice PL ISSN 1642-5308 NOWOCZESNE ODMIANY ŻELIWA O STRUKTURZE AUSFERRYTYCZNEJ A.
Bardziej szczegółowoWykaz linii kolejowych, które są wyposażone w urzadzenia systemu ETCS
Wykaz kolejowych, które są wyposażone w urzadzenia W tablicy znajdującej się na kolejnych stronach tego załącznika zastosowano następujące oznaczenia: - numer kolejowej według instrukcji Wykaz Id-12 (D-29).
Bardziej szczegółowoEGZAMIN MATURALNY Z JĘZYKA ANGIELSKIEGO
Miejsce na naklejkę z kodem szkoły dysleksja MJA-R1_1P-072 EGZAMIN MATURALNY Z JĘZYKA ANGIELSKIEGO MAJ ROK 2007 Instrukcja dla zdającego POZIOM ROZSZERZONY CZĘŚĆ I Czas pracy 120 minut 1. Sprawdź, czy
Bardziej szczegółowoALA MA KOTA PRESCHOOL URSYNÓW WARSAW POLAND
ALA MA KOTA PRESCHOOL URSYNÓW WARSAW POLAND Ala ma kota is a network of non-public education preschools which are entered into the register of non-public schools and institutions of the Capital City of
Bardziej szczegółowoPlease note, this is only a guide and I will not be held responsible if you fuck it up!!!
Please note, this is only a guide and I will not be held responsible if you fuck it up!!! Autorem jest niejaki zed [przyp.tł.] Proszę wziąć pod uwagę, że to są jedynie wskazówki. Nie będę poczuwał się
Bardziej szczegółowoAkademia Morska w Szczecinie. Wydział Mechaniczny
Akademia Morska w Szczecinie Wydział Mechaniczny ROZPRAWA DOKTORSKA mgr inż. Marcin Kołodziejski Analiza metody obsługiwania zarządzanego niezawodnością pędników azymutalnych platformy pływającej Promotor:
Bardziej szczegółowoRozpoznawanie twarzy metodą PCA Michał Bereta 1. Testowanie statystycznej istotności różnic między jakością klasyfikatorów
Rozpoznawanie twarzy metodą PCA Michał Bereta www.michalbereta.pl 1. Testowanie statystycznej istotności różnic między jakością klasyfikatorów Wiemy, że możemy porównywad klasyfikatory np. za pomocą kroswalidacji.
Bardziej szczegółowoAdres do korespondencji: Instytut Metalurgii i Inżynierii Materiałowej PAN, Kraków, ul. Reymonta 25
Adres do korespondencji: Instytut Metalurgii i Inżynierii Materiałowej PAN, 30059 Kraków, ul. Reymonta 25 Tel.: (012) 295 28 70, pokój 104, fax: (012) 295 28 04, email: p.petrzak@imim.pl Miejsca zatrudnienia
Bardziej szczegółowoM210 SNKX1205 SNKX1607. Stable face milling under high-load conditions Stabilna obróbka przy wysokich posuwach FACE MILLING CUTTERS
Stable face milling under high-load conditions Stabilna obróbka przy wysokich posuwach SNKX1205 SNKX1607 FACE MILLING CUTTERS FREZY DO OBRÓBKI PŁASZCZYZN SNKX1205/1607 FACE MILLING CUTTERS FREZY DO OBRÓBKI
Bardziej szczegółowoZestawienie czasów angielskich
Zestawienie czasów angielskich Present Continuous I am, You are, She/ He/ It is, We/ You/ They are podmiot + operator + (czasownik główny + ing) + reszta I' m driving. operator + podmiot + (czasownik główny
Bardziej szczegółowoProposal of thesis topic for mgr in. (MSE) programme in Telecommunications and Computer Science
Proposal of thesis topic for mgr in (MSE) programme 1 Topic: Monte Carlo Method used for a prognosis of a selected technological process 2 Supervisor: Dr in Małgorzata Langer 3 Auxiliary supervisor: 4
Bardziej szczegółowo12x50 two-wing pivot screw-in hinges
x dwuskrzydełkowe śruby wysokość ; mosiądz; surowy x two-wing pivot screw-in hinges bolt height ; brass; raw two-wing pivot screw-in xx35 śruby wysokość 56 czopowe wciskano-wkręcane x35 hinges bolt height
Bardziej szczegółowoMiedzy legenda a historia: Szlakiem piastowskim z Poznania do Gniezna (Biblioteka Kroniki Wielkopolski) (Polish Edition)
Miedzy legenda a historia: Szlakiem piastowskim z Poznania do Gniezna (Biblioteka Kroniki Wielkopolski) (Polish Edition) Piotr Maluskiewicz Click here if your download doesn"t start automatically Miedzy
Bardziej szczegółowoUkryte funkcjonalności w oprogramowaniu i urządzeniach elektronicznych. mgr inż. Paweł Koszut
Ukryte funkcjonalności w oprogramowaniu i urządzeniach elektronicznych mgr inż. Paweł Koszut Ukryte funkcjonalności w oprogramowaniu i urządzeniach elektronicznych Zamiast wstępu : Inspiracja GSM w Grecji
Bardziej szczegółowoDolny Slask 1: , mapa turystycznosamochodowa: Plan Wroclawia (Polish Edition)
Dolny Slask 1:300 000, mapa turystycznosamochodowa: Plan Wroclawia (Polish Edition) Click here if your download doesn"t start automatically Dolny Slask 1:300 000, mapa turystyczno-samochodowa: Plan Wroclawia
Bardziej szczegółowoWojewodztwo Koszalinskie: Obiekty i walory krajoznawcze (Inwentaryzacja krajoznawcza Polski) (Polish Edition)
Wojewodztwo Koszalinskie: Obiekty i walory krajoznawcze (Inwentaryzacja krajoznawcza Polski) (Polish Edition) Robert Respondowski Click here if your download doesn"t start automatically Wojewodztwo Koszalinskie:
Bardziej szczegółowoWPŁYW TEMPERATURY WYGRZEWANIA NA UDZIAŁ FAZ PIERWOTNYCH W STRUKTURZE ŻAROWYTRZYMAŁEGO ODLEWNICZEGO STOPU KOBALTU
50/22 Archives of Foundry, Year 2006, Volume 6, 22 Archiwum Odlewnictwa, Rok 2006, Rocznik 6, Nr 22 PAN Katowice PL ISSN 1642-5308 WPŁYW TEMPERATURY WYGRZEWANIA NA UDZIAŁ FAZ PIERWOTNYCH W STRUKTURZE ŻAROWYTRZYMAŁEGO
Bardziej szczegółowo