THERMODYNAMICS OF OXYGEN IN DILUTE LIQUID SILVER-TELLURIUM ALLOYS
|
|
- Maja Mucha
- 5 lat temu
- Przeglądów:
Transkrypt
1 AGH University of Science and Technology Faculty of Non-Ferrous Metals Laboratory of Physical Chemistry and Electrochemistry THERMODYNAMICS OF OXYGEN IN DILUTE LIQUID SILVER-TELLURIUM ALLOYS Justyna Nyk, Bogusław Onderka, Krzysztof Fitzner
2 MOTIVATION ANODIC SLIME a by-product of the electrolytic refining of copper. ANODIC SLIME a source of silver, gold, platinum group metals, selenium and tellurium. Composition of anodic slime silver Gold, Pt-group selenium, tellurium
3 DIAGRAM OF SILVER PROCESSING Electrolytic refining of copper Cu Slime containing Ag Treatment of anodic slime Kaldo furnace charge Kaldo furnace
4 DIAGRAM OF SILVER PROCESSING Kaldo furnace Oxidation Refining Removal of Te by sodium carbonate Electrolytic refining of silver Ag
5 Refining of silver 1 OXIDATION 2 REMOVAL OF SELENIUM 3 REMOVAL OF TELLURIUM
6 Tellurium elimination from Ag The tellurium elimination by oxidation: [ Te ] + 2 [ O ] = ( TeO ) + = (1) Ag Ag 2 slag L slag / Ag Te γ [ Te ] ( n) Ag slag = K 1 γ [ n] TeO 2 Ag a 2 [ O ] Ag (2)
7 Tellurium elimination by sodium carbonate Product of reaction depends on oxygen pressure: - In reducing conditions product is sodium telluride (Na 2 Te): [ ] ( ) Te + Na CO = Na Te + CO + 0.5O Ag slag 2 2 (3) - In oxidizing conditions product is sodium tellurate (Na 2 TeO 3 ): [ ] ( ) Te + Na CO + O = Na TeO + CO (4) Ag slag 2 M.Perez-Tello and M.Prito-Sanchez, A Kinetic Model for the Oxidation of Selenium and Tellurium in an Industrial Kaldo Furnace,JOM, 56(12), (2004)
8 Removal of tellurium by sodium carbonate Distribution coefficient of tellurium between slag and metallic phase for reaction (3) and (4): - Reducing conditions: log L = - 1 2log a + slag / Ag Te,(3) [ O] Ag const (5) - Oxidizing conditions: log L = log a + slag / Ag Te,(4) [ O] Ag const (6) For constant P CO2 and temperature an activity of Na 2 CO 3 was assumed to be 1 (n Na >> n Te ).
9 Oxygen activity determination The coulometric titration measurements of galvanic cell with YSZ solid oxide electrolyte: Ag-(Te)-O ZrO 2 +Y 2 O 3 O 2 (in air) P O 2 P O 2 = bar (I) Method aim: Determination of effect of tellurium concentration on the activity coefficient of oxygen in dilute liquid Ag alloys - (γ o Ag ) in defined temperature range.
10 Scheme of assembly <3> <2> <1> Fig 1. The scheme of electrochemical cell assembly for the coulometric titration measurements.
11 Examplesof changeof electric current with time for experiments with liquid silver tellurium alloys 2% at. Te 4% at. Te T=1285 K T=1285 K Q= C Q= C
12 Theoretical basis The coulometric titration method bases on measure of EMF change dependent on partial pressure of oxygen, as follows: E 1 R T 0.21 = ln 4 F p O 2 (7) Activity coefficient of oxygen γ 0 in liquid metallic phase: O 1/2 2 γ = (8) 0 (p ) C 1
13 Theoretical basis The change of concentration of oxygen in sample during titration experiment: 100 M Q jon C1 C2 = (9) 2 W F Activity coefficient of oxygen γ 0 in liquid solution: γ 0 2E F 0.21 ln R T C 1 1 = exp + (10) The standard Gibbs free energy of oxygen dissolution in liquid metallic melt: G = RT ln γ (11) 0 O 0
14 Experimental results I. Measurements of activity coefficient of oxygen in liquid silver reference and test of this method.
15 Experimental results for pure liquid Ag Experimental temperature range: K (step: 50 K) Table 2. The example of obtained results at 1285 K T= 1285, K G E 0 O, 1, V E 2, V Q jon, C C 1, at. % O ln γ O O J/mol
16 Temperature dependence of standard free energy of oxygen dissolution in pure liquid Ag Fig. 2.
17 II. Measurements of activity coefficient of oxygen for dilute liquid Ag-Te-O alloys
18 Phase diagram of Ag-Te Experimental Te concentration range was limited to dilute liquid solution of Te in Ag Temperature e, 0 C L 1 +FCC L 1 LIQUID L 1 + L 2 L 1 + Ag 2 Te L 2 FCC + Ag 2 Te L 2 + Ag 2 Te Ag mole %Te mole %Te Fig. 3.
19 Experimental results for dilute liquid Ag-Te-O alloys Table 3. Experimental results for 2 at.% Te liquid Ag-Te-O alloy. T = 1385 K No. E 1, V E 2, V Q jon, C C 1, at. % O G ln γ 0 O, O o J/mol
20 Experimental results for dilute liquid Ag-Te-O alloys - example for two tellurium concentrations in Ag-Te-O alloys. 2 at. % Te 3 at. % Te Fig. 4. The standard Gibbs free energy of oxygen dissolution in Ag-Te liquid solution as a function of temperature.
21 Interpretation The change in oxygen activity coefficient in dilute solution caused by the addition of the other metallic component defined as a function of Te concentration: 0 (Te) O O O O Te ln γ = ln γ ln γ = ε X where: (Te) lnγ ε O O = X Ag Te X 1 is a first order interaction parameter. The mole fraction of tellurium addition is denoted by X Te.
22 ln γ o vs. X Te and temperature dependence Table 4. ln γ o vs. X Te and temperature dependence (0 < X Te < 0.06) 1285K 1335 K 1385 K 1435 K 1485 K X Te lnγ o lnγ o lnγ o lnγ o lnγ o
23 lnγ o vs. X Te dependence (0 < X Te < 0.06) determined for different T values 1385 K 1335 K Fig.5. The dependence of ln γ o vs. X Te (0 < X Te 0.06) determined for different temperatures.
24 Temperature dependence of a first-order interaction parameter ε O Te Table 5. T, K 1/T, K -1 Te ε O , , , , , Fig. 6. Interaction parameterε O Te as a function of (1/T).
25 Conclusions 1. The standard free energy of oxygen dissolution in liquid Ag-Te alloys showed negative values. Its absolute value increases with increase of Te concentration and decreases with the growth of temperature. 2. At given temperature tellurium concentration enlargement causes the depression of activity coefficient of oxygen in liquid Ag-Te solutions.
26 Influence of lead on thermodynamics of oxygen in Ag-Te liquid solutions Some hot results Ag-Te-Pb-O alloy Ag-Te-O alloy 4 at. % Te 10 at. % Pb 4 at. % Te
27 THANK YOU FOR YOUR ATTENTION
28
29
30
31 Wnioski 1. Energia swobodna Gibbsa rozpuszczania tlenu w ciekłym roztworze Ag-Te ma wartości ujemne i jej wartość bezwzględna rośnie z zawartością telluru i maleje ze wzrostem temperatury. 2. W danej temperaturze wzrost stężenia telluru powoduje obniżenie współczynnika aktywności tlenu w ciekłym roztworze. Oznacza to zmniejszenie rozpuszczalności tlenu w ciekłym roztworze Ag z dodatkiem telluru.
32 lnγ o vs. X Te dependence (0 < X Te < 0.06) determined for different T values 1335 K 1385 K Fig.5. The dependence of ln γ o vs. X Te (0 < X Te 0.06) determined for different temperatures. 90% confidence intervals were calculated.
33 Scheme of the cell air Fig 2. Scheme of solid oxide galvanic cell.
34 Distribution Coefficient The distribution coefficient describes the partition accompanying elements between slag and metal and is therefore an indicator for the efficiency of the metal extraction [8]. (1) In the slag the different metals M (e.g. Cu, Ni, Zn, Pb, Sn etc.) exist in the form of oxides, as demonstrated by the reaction in equation 2. Equation 3 shows the corresponding equilibrium constant to this reaction. The distribution coefficient is directly proportional to p O2 n/2 if the behavior of the metal M in the copper and of the metal oxide MO in the slag obeys Henry`s law.
35 The distribution coefficient of a solute between two The distribution coefficient of a solute between two phases is calculated as the ratio of the concentration of the solute in one phase to the concentration of the solute in the other phase under equilibrium conditions.
36 Usuwanie telluru za pomocą sody W atmosferze redukcyjnej tellur można usunąć jako tellurek sodu Na 2 Te. Metodę tą opisuje reakcja: [ ] ( ) Te + Na CO = Na Te + CO + 0.5O Ag żużel 2 2 Współczynnik podziału telluru między fazę żużlową i metaliczną: K g żużel / Ag 2 [ Te] Ag żużel log LTe = log + log ana2 ( CO3 ) g Na Te[ n] Ag 2 ( n) æ1 ö - ç log po - log çè 2 ø p CO 2 2 (2) Aktywność Na 2 CO 3 można przyjąć za równą 1, co dla ustalonego ciśnienia parcjalnego CO 2 i temperatury prowadzi do zależności: log żużel / Ag LTe,(2) = - 1 2log a[ O] + const Ag
37 Usuwanie telluru za pomocą sody W atmosferze utleniającej tellur można usunąć jako telluryn sodu Na 2 TeO Metodę tą opisuje reakcja: [ ] ( ) Te + Na CO + O = Na TeO + CO Ag żużel 2 Współczynnik podziału telluru między fazę żużlową i metaliczną: K g żużel / Ag 3 [ Te] Ag żużel log LTe = log + log ana2 ( CO3 ) g Na TeO [ n] Ag 2 3 ( n) æ1 ö - ç log po + log çè 2 ø p CO 2 2 (3) Aktywność Na 2 CO 3 można przyjąć za równą 1, co dla ustalonego ciśnienia parcjalnego CO 2 i temperatury prowadzi do zależności: log L = log a + żużel / Ag Te,(3) [ O] Ag const
38 SCHEMAT PRODUKCJI SREBRA
H γ0 - the standard enthalpy of g phase. H β γ - the transition enthalpy of b to g
H α0 - the standard enthalpy of a phase H β0 - the standard enthalpy of b phase H γ0 - the standard enthalpy of g phase H α β - the transition enthalpy of a to b phase at T t1 H β γ - the transition enthalpy
Bardziej szczegółowoSlag number kw x TeO
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 59 14 Issue 1 DOI: 1.478/amm-14-9 M. KUCHARSKI, P. MADEJ, M. WĘDRYCHOWICZ, T. SAK, W. MRÓZ RECOVERY OF TELLURIUM FROM SODIUM CARBONATE
Bardziej szczegółowoWPŁYW STĘŻENIA WODOROTLENKU SODOWEGO NA ROZPUSZCZALNOŚĆ TLENU W ROZTWORACH WODNYCH
INŻYNIERIA CHEMICZNA I PROCESOWA 22(3):717-722 (2001) HANNA KIERZKOWSKA-PAWLAK, GRZEGORZ WIELGOSIŃSKI WPŁYW STĘŻENIA WODOROTLENKU SODOWEGO NA ROZPUSZCZALNOŚĆ TLENU W ROZTWORACH WODNYCH Politechnika Łódzka,
Bardziej szczegółowo200 years of Henry s law (1803)!!! In a two component system (liquid + gas), at T=const., 1 degree of freedom exists, then pressure defines the state
1 200 years of Henry s law (1803)!!! In a two component system (liquid + gas), at T=const., 1 degree of freedom exists, then pressure defines the state of the system unambiguously. Pressure of liquid vapour
Bardziej szczegółowoTytuł pracy w języku angielskim: Microstructural characterization of Ag/X/Ag (X = Sn, In) joints obtained as the effect of diffusion soledering.
Dr inż. Przemysław Skrzyniarz Kierownik pracy: Prof. dr hab. inż. Paweł Zięba Tytuł pracy w języku polskim: Charakterystyka mikrostruktury spoin Ag/X/Ag (X = Sn, In) uzyskanych w wyniku niskotemperaturowego
Bardziej szczegółowoFig 5 Spectrograms of the original signal (top) extracted shaft-related GAD components (middle) and
Fig 4 Measured vibration signal (top). Blue original signal. Red component related to periodic excitation of resonances and noise. Green component related. Rotational speed profile used for experiment
Bardziej szczegółowoTYRE PYROLYSIS. REDUXCO GENERAL DISTRIBUTOR :: ::
TYRE PYROLYSIS Installation for rubber waste pyrolysis designed for processing of used tyres and plastic waste (polyethylene, polypropylene, polystyrene), where the final product could be electricity,
Bardziej szczegółowoKnovel Math: Jakość produktu
Knovel Math: Jakość produktu Knovel jest agregatorem materiałów pełnotekstowych dostępnych w formacie PDF i interaktywnym. Narzędzia interaktywne Knovel nie są stworzone wokół specjalnych algorytmów wymagających
Bardziej szczegółowoWPŁYW WARUNKÓW PRZESYCANIA I STARZENIA STOPU C355 NA ZMIANY JEGO TWARDOŚCI
40/15 Archives of Foundry, Year 2005, Volume 5, 15 Archiwum Odlewnictwa, Rok 2005, Rocznik 5, Nr 15 PAN Katowice PL ISSN 1642-5308 WPŁYW WARUNKÓW PRZESYCANIA I STARZENIA STOPU C355 NA ZMIANY JEGO TWARDOŚCI
Bardziej szczegółowoFew-fermion thermometry
Few-fermion thermometry Phys. Rev. A 97, 063619 (2018) Tomasz Sowiński Institute of Physics of the Polish Academy of Sciences Co-authors: Marcin Płodzień Rafał Demkowicz-Dobrzański FEW-BODY PROBLEMS FewBody.ifpan.edu.pl
Bardziej szczegółowoMedical electronics part 10 Physiological transducers
Medical electronics part 10 Prezentacja multimedialna współfinansowana przez Unię Europejską w ramach Europejskiego Funduszu Społecznego w projekcie pt. Innowacyjna dydaktyka bez ograniczeń - zintegrowany
Bardziej szczegółowotum.de/fall2018/ in2357
https://piazza.com/ tum.de/fall2018/ in2357 Prof. Daniel Cremers From to Classification Categories of Learning (Rep.) Learning Unsupervised Learning clustering, density estimation Supervised Learning learning
Bardziej szczegółowoConception of reuse of the waste from onshore and offshore in the aspect of
Conception of reuse of the waste from onshore and offshore in the aspect of environmental protection" Koncepcja zagospodarowania odpadów wiertniczych powstających podczas wierceń lądowych i morskich w
Bardziej szczegółowoMachine Learning for Data Science (CS4786) Lecture 11. Spectral Embedding + Clustering
Machine Learning for Data Science (CS4786) Lecture 11 Spectral Embedding + Clustering MOTIVATING EXAMPLE What can you say from this network? MOTIVATING EXAMPLE How about now? THOUGHT EXPERIMENT For each
Bardziej szczegółowoThe Lorenz System and Chaos in Nonlinear DEs
The Lorenz System and Chaos in Nonlinear DEs April 30, 2019 Math 333 p. 71 in Chaos: Making a New Science by James Gleick Adding a dimension adds new possible layers of complexity in the phase space of
Bardziej szczegółowoKiedy przebiegają reakcje?
Kiedy przebiegają reakcje? Thermodynamics lets us predict whether a process will occur but gives no information about the amount of time required for the process. CH 4(g) + 2O 2(g) substraty 2(g) egzotermiczna
Bardziej szczegółowoMetodyki projektowania i modelowania systemów Cyganek & Kasperek & Rajda 2013 Katedra Elektroniki AGH
Kierunek Elektronika i Telekomunikacja, Studia II stopnia Specjalność: Systemy wbudowane Metodyki projektowania i modelowania systemów Cyganek & Kasperek & Rajda 2013 Katedra Elektroniki AGH Zagadnienia
Bardziej szczegółowoA R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume Issue 1 DOI: /v y
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 57 2012 Issue 1 DOI: 10.2478/v10172-011-0149-y G. BOCZKAL, P. MARECKI, M. PEREK-NOWAK THE INFLUENCE OF SOLDERING CONDITIONS ON CONDUCTIVITY,
Bardziej szczegółowoANDRZEJ GONTARZ, ANNA DZIUBIŃSKA
ANDRZEJ GONTARZ, ANNA DZIUBIŃSKA Politechnika Lubelska, Katedra Komputerowego Modelowania i Technologii Obróbki Plastycznej ul. Nadbystrzycka 36, 20-618 Lublin a.gontarz@pollub.pl Własności stopu magnezu
Bardziej szczegółowoModel standardowy i stabilność próżni
Model standardowy i stabilność próżni Marek Lewicki Instytut Fizyki teoretycznej, Wydzia l Fizyki, Uniwersytet Warszawski Sympozjum Doktoranckie Warszawa-Fizyka-Kraków, 4 Marca 2016, Kraków Na podstawie:
Bardziej szczegółowoThe temperature measurements Pomiary temperatur
Silesian University of Technology Faculty of Energy and Environmental Engineering Politechnika Śląska Wydział Inżynierii Środowiska I Energetyki Instytut Maszyn I Urządzeń Energetycznych The temperature
Bardziej szczegółowoAdres do korespondencji: Instytut Metalurgii i Inżynierii Materiałowej PAN, Kraków, ul. Reymonta 25
Adres do korespondencji: Instytut Metalurgii i Inżynierii Materiałowej PAN, 30059 Kraków, ul. Reymonta 25 Tel.: (012) 295 28 14, pokój 214, fax: (012) 295 28 04 email: a.debski@imim.pl Miejsca zatrudnienia
Bardziej szczegółowoKRYSTALIZACJA I MIKROSTRUKTURA BRĄZU CuAl10Fe5Ni5 PO RAFINACJI
55/17 ARCHIWUM ODLEWNICTWA Rok 2005, Rocznik 5, Nr 17 Archives of Foundry Year 2005, Volume 5, Book 17 PAN - Katowice PL ISSN 1642-5308 KRYSTALIZACJA I MIKROSTRUKTURA BRĄZU CuAl10Fe5Ni5 PO RAFINACJI S.
Bardziej szczegółowoSTRUKTURA STOPÓW UKŁADY RÓWNOWAGI FAZOWEJ. Publikacja współfinansowana ze środków Unii Europejskiej w ramach Europejskiego Funduszu Społecznego
STRUKTURA STOPÓW UKŁADY RÓWNOWAGI FAZOWEJ Publikacja współfinansowana ze środków Unii Europejskiej w ramach Europejskiego Funduszu Społecznego Wykresy układów równowagi faz stopowych Ilustrują skład fazowy
Bardziej szczegółowoA R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume Issue 4 DOI: /v
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 55 2010 Issue 4 DOI: 10.2478/v10172-010-0013-5 J. FALKUS, L. TRĘBACZ, B. ZAWADA UTILIZATION OF THE STEELMAKING SLAG BY REDUCTION WITH
Bardziej szczegółowoPrices and Volumes on the Stock Market
Prices and Volumes on the Stock Market Krzysztof Karpio Piotr Łukasiewicz Arkadiusz Orłowski Warszawa, 25-27 listopada 2010 1 Data selection Warsaw Stock Exchange WIG index assets most important for investors
Bardziej szczegółowoDUAL SIMILARITY OF VOLTAGE TO CURRENT AND CURRENT TO VOLTAGE TRANSFER FUNCTION OF HYBRID ACTIVE TWO- PORTS WITH CONVERSION
ELEKTRYKA 0 Zeszyt (9) Rok LX Andrzej KUKIEŁKA Politechnika Śląska w Gliwicach DUAL SIMILARITY OF VOLTAGE TO CURRENT AND CURRENT TO VOLTAGE TRANSFER FUNCTION OF HYBRID ACTIVE TWO- PORTS WITH CONVERSION
Bardziej szczegółowoUnit of Social Gerontology, Institute of Labour and Social Studies ageing and its consequences for society
Prof. Piotr Bledowski, Ph.D. Institute of Social Economy, Warsaw School of Economics local policy, social security, labour market Unit of Social Gerontology, Institute of Labour and Social Studies ageing
Bardziej szczegółowoA R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume Issue 4
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 54 2009 Issue 4 D. LEŚNIAK STRUCTURE AND MECHANICAL PROPERTIES OF EXTRUDED AlCuMg SECTIONS IN T5 TEMPER STRUKTURA I WŁASNOŚCI MECHANICZNE
Bardziej szczegółowoAdres do korespondencji: Instytut Metalurgii i Inżynierii Materiałowej PAN, Kraków, ul. Reymonta 25
Adres do korespondencji: Instytut Metalurgii i Inżynierii Materiałowej PAN, 30059 Kraków, ul. Reymonta 25 Tel.: (012) 295 28 14, pokój 214, fax: (012) 295 28 04 email: a.debski@imim.pl Miejsca zatrudnienia
Bardziej szczegółowoA NEW METHOD OF MEASURING THE OPERATING PARAMETERS OF SLIDE JOURNAL BEARINGS BY USING ACOUSTIC EMISSION
6-2009 T R I B O L O G I A 165 Burkhard ZIEGLER *, Krzysztof WIERZCHOLSKI **, Andrzej MISZCZAK *** A NEW METHOD OF MEASURING THE OPERATING PARAMETERS OF SLIDE JOURNAL BEARINGS BY USING ACOUSTIC EMISSION
Bardziej szczegółowoWhere does value of smelter come from? Case study based on KGHM perspective 27th International Copper Conference, Milan, March 10-12, 2014
Where does value of smelter come from? Case study based on KGHM perspective 27th International Copper Conference, Milan, March 10-12, 2014 Artur Więznowski Jerzy Lisak Areas covered in the presentation:
Bardziej szczegółowoOdpowietrznik / Vent Charakterystyka pracy / Performance characteristic: Wykres ciœnienia wyjœciowego p2 w funkcji ciœnienia steruj¹cego p4 Diagram -
Zawór hamowania przyczepy 45 10 Trailer control valve Przeznaczenie: Zawór steruj¹cy przyczepy stosowany jest w jednoprzewodowych i kombinowanych powietrznych uk³adach hamulcowych pojazdów samochodowych
Bardziej szczegółowoLecture 18 Review for Exam 1
Spring, 2019 ME 323 Mechanics of Materials Lecture 18 Review for Exam 1 Reading assignment: HW1-HW5 News: Ready for the exam? Instructor: Prof. Marcial Gonzalez Announcements Exam 1 - Wednesday February
Bardziej szczegółowoOpenPoland.net API Documentation
OpenPoland.net API Documentation Release 1.0 Michał Gryczka July 11, 2014 Contents 1 REST API tokens: 3 1.1 How to get a token............................................ 3 2 REST API : search for assets
Bardziej szczegółowoOBRÓBKA CIEPLNA SILUMINU AK132
52/22 Archives of Foundry, Year 2006, Volume 6, 22 Archiwum Odlewnictwa, Rok 2006, Rocznik 6, Nr 22 PAN Katowice PL ISSN 1642-5308 OBRÓBKA CIEPLNA SILUMINU AK132 J. PEZDA 1 Akademia Techniczno-Humanistyczna
Bardziej szczegółowoTHEORETICAL STUDIES ON CHEMICAL SHIFTS OF 3,6 DIIODO 9 ETHYL 9H CARBAZOLE
THEORETICAL STUDIES ON CHEMICAL SHIFTS OF 3,6 DIIODO 9 ETHYL 9H CARBAZOLE Teobald Kupkaa, Klaudia Radula-Janika, Krzysztof Ejsmonta, Zdzisław Daszkiewicza, Stephan P. A. Sauerb a Faculty of Chemistry,
Bardziej szczegółowoA NEW MEASUREMENT METHOD OF FRICTION FORCES REGARDING SLIDE JOURNAL BEARINGS BY ACOUSTIC EMISSION
1-2010 T R I B O L O G I A 149 Burkhard ZIEGLER *, Krzysztof WIERZCHOLSKI **, Andrzej MISZCZAK *** A NEW MEASUREMENT METHOD OF FRICTION FORCES REGARDING SLIDE JOURNAL BEARINGS BY ACOUSTIC EMISSION NOWE
Bardziej szczegółowoDETERMINATION OF TEMPERATURE DISTRIBUTION IN ACTIVE COVERING DURING PRODUCING OF COATINGS BY CASTING METHOD.
29/38 Solidification of Metals and Alloys, No. 38, 1998 Krzepnięcie Metali i Stopów, nr 38, 1998 PAN Katowice PL ISSN 0208-9386 DETERMINATION OF TEMPERATURE DISTRIBUTION IN ACTIVE COVERING DURING PRODUCING
Bardziej szczegółowoWPŁYW RÓŻNOWARTOŚCIOWYCH DOMIESZEK NA SZYBKOŚĆ WZROSTU ZGORZELIN NA METALACH (TEORIA HAUFFEGO-WAGNERA)
WPŁYW RÓŻNOWARTOŚCIOWYCH DOMIEZEK NA ZYBKOŚĆ WZROTU ZGORZELIN NA METALACH (TEORIA HAUFFEGO-WAGNERA) 1. K. Hauffe, Progress in Metal Physic, 4, 71 (1953).. P. Kofstad, Nonstoichiometry, diffusion and electrical
Bardziej szczegółowoTytuł pracy w języku angielskim: Physical properties of liquid crystal mixtures of chiral and achiral compounds for use in LCDs
Dr inż. Jan Czerwiec Kierownik pracy: dr hab. Monika Marzec Tytuł pracy w języku polskim: Właściwości fizyczne mieszanin ciekłokrystalicznych związków chiralnych i achiralnych w odniesieniu do zastosowań
Bardziej szczegółowoCENTRUM CZYSTYCH TECHNOLOGII WĘGLOWYCH CLEAN COAL TECHNOLOGY CENTRE. ... nowe możliwości. ... new opportunities
CENTRUM CZYSTYCH TECHNOLOGII WĘGLOWYCH CLEAN COAL TECHNOLOGY CENTRE... nowe możliwości... new opportunities GŁÓWNY INSTYTUT GÓRNICTWA fluidalnym przy ciśnieniu maksymalnym 5 MPa, z zastosowaniem różnych
Bardziej szczegółowoWtrącenia niemetaliczne w staliwie topionym w małym piecu indukcyjnym
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (897-0) Volume Special Issue /0 9 97 8/ Wtrącenia
Bardziej szczegółowoBADANIA ABSORPCJI GAZÓW W UKŁADACH DWUFAZOWYCH CIEKŁYCH
INŻYNIERIA CHEMICZNA I PROCESOWA T. 25, Z. 3/2, 1095--1100 (2004) HANNA KIERZKOWSKA-PAWLAK, DOROTA WŁODARCZYK, ROMAN ZARZYCKI BADANIA ABSORPCJI GAZÓW W UKŁADACH DWUFAZOWYCH CIEKŁYCH Politechnika Łódzka,
Bardziej szczegółowo4. EKSPLOATACJA UKŁADU NAPĘD ZWROTNICOWY ROZJAZD. DEFINICJA SIŁ W UKŁADZIE Siła nastawcza Siła trzymania
3 SPIS TREŚCI Przedmowa... 11 1. WPROWADZENIE... 13 1.1. Budowa rozjazdów kolejowych... 14 1.2. Napędy zwrotnicowe... 15 1.2.1. Napęd zwrotnicowy EEA-4... 18 1.2.2. Napęd zwrotnicowy EEA-5... 20 1.3. Współpraca
Bardziej szczegółowoProposal of thesis topic for mgr in. (MSE) programme in Telecommunications and Computer Science
Proposal of thesis topic for mgr in (MSE) programme 1 Topic: Monte Carlo Method used for a prognosis of a selected technological process 2 Supervisor: Dr in Małgorzata Langer 3 Auxiliary supervisor: 4
Bardziej szczegółowoKiedy przebiegają reakcje?
Kiedy przebiegają reakcje? Thermodynamics lets us predict whether a process will occur but gives no information about the amount of time required for the process. Termodynamika dziedzina termodynamiki
Bardziej szczegółowoZMNIEJSZENIE NEGATYWNYCH SKUTKÓW DEPONOWANIA W ŚRODOWISKU ODPADÓW Z INSTALACJI ODSIARCZANIA SPALIN
Progress in Plant Protection / Postępy w Ochronie Roślin, 46 (2) 2006 ZMNIEJSZENIE NEGATYWNYCH SKUTKÓW DEPONOWANIA W ŚRODOWISKU ODPADÓW Z INSTALACJI ODSIARCZANIA SPALIN PIOTR GRZESIAK, MARCIN GROBELA,
Bardziej szczegółowoMikroskopia polowa. Efekt tunelowy Historia odkryć Uwagi o tunelowaniu Zastosowane rozwiązania. Bolesław AUGUSTYNIAK
Mikroskopia polowa Efekt tunelowy Historia odkryć Uwagi o tunelowaniu Zastosowane rozwiązania Bolesław AUGUSTYNIAK Efekt tunelowy Efekt kwantowy, którym tłumaczy się przenikanie elektronu w sposób niezgodny
Bardziej szczegółowoBADANIE KRYSTALIZACJI KOMPOZYTU AK9-Pb. Z. KONOPKA 1 Katedra Odlewnictwa Politechniki Częstochowskiej
5/44 Solidification of Metals and Alloys, Year, Volume, Book No. 44 Krzepnięcie Metali i Stopów, Rok, Rocznik, Nr 44 PAN Katowice PL ISSN 8-9386 BADANIE KRYSALIZACJI KOMPOZYU AK9-Pb Z. KONOPKA Katedra
Bardziej szczegółowoBIOPHYSICS. Politechnika Łódzka, ul. Żeromskiego 116, Łódź, tel. (042)
BIOPHYSICS Prezentacja multimedialna współfinansowana przez Unię Europejską w ramach Europejskiego Funduszu Społecznego w projekcie pt. Innowacyjna dydaktyka bez ograniczeń - zintegrowany rozwój Politechniki
Bardziej szczegółowoAdres do korespondencji: Instytut Metalurgii i Inżynierii Materiałowej PAN, Kraków, ul. Reymonta 25
Adres do korespondencji: Instytut Metalurgii i Inżynierii Materiałowej PAN, 30059 Kraków, ul. Reymonta 25 Tel.: (012) 295 28 14, pokój 214, fax: (012) 295 28 04 email: a.debski@imim.pl Miejsca zatrudnienia
Bardziej szczegółowoInverse problems - Introduction - Probabilistic approach
Inverse problems - Introduction - Probabilistic approach Wojciech Dȩbski Instytut Geofizyki PAN debski@igf.edu.pl Wydział Fizyki UW, 13.10.2004 Wydział Fizyki UW Warszawa, 13.10.2004 (1) Plan of the talk
Bardziej szczegółowoElektrochemia - prawa elektrolizy Faraday a. Zadania
Elektrochemia - prawa elektrolizy Faraday a Zadania I prawo Faraday a Masa substancji wydzielonej na elektrodach podczas elektrolizy jest proporcjonalna do natężenia prądu i czasu trwania elektrolizy q
Bardziej szczegółowooraz stężenie ceruloplazminy (CER)), stresu oksydacyjnego ((stężenie dialdehydu malonowego (MDA), stężenie nadtlenków lipidowych (LPH) i całkowity
STRESZCZENIE Pola elektromagnetyczne może prowadzić do powstania w organizmie żywym stresu oksydacyjnego, który powoduje wzrost stężenia reaktywnych form tlenu, zmianę aktywności układów antyoksydacyjnych,
Bardziej szczegółowoO 2 ions are formed in the reaction:
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 59 2014 Issue 1 DOI: 10.2478/amm-2014-0022 W. GUMOWSKA, I. DOBOSZ, B. WRZOSZCZYK THE MORPHOLOGY OF THE ALUMINA FILMS FORMED IN THE
Bardziej szczegółowoWeronika Mysliwiec, klasa 8W, rok szkolny 2018/2019
Poniższy zbiór zadań został wykonany w ramach projektu Mazowiecki program stypendialny dla uczniów szczególnie uzdolnionych - najlepsza inwestycja w człowieka w roku szkolnym 2018/2019. Tresci zadań rozwiązanych
Bardziej szczegółowoNazwa projektu: Kreatywni i innowacyjni uczniowie konkurencyjni na rynku pracy
Nazwa projektu: Kreatywni i innowacyjni uczniowie konkurencyjni na rynku pracy DZIAŁANIE 3.2 EDUKACJA OGÓLNA PODDZIAŁANIE 3.2.1 JAKOŚĆ EDUKACJI OGÓLNEJ Projekt współfinansowany przez Unię Europejską w
Bardziej szczegółowoWPŁYW MIESZANKI EGZOTERMICZNEJ NA BAZIE Na 2 B 4 O 7 I NaNO 3 NA WYTRZYMAŁOŚĆ NA ROZCIĄGANIE STOPU AlSi7Mg
4/ Archives of Foundry, Year 006, Volume 6, Archiwum Odlewnictwa, Rok 006, Rocznik 6, Nr PAN Katowice PL ISSN 64-508 WPŁYW MIESZANKI EGZOTERMICZNEJ NA BAZIE Na B 4 O 7 I NaNO NA WYTRZYMAŁOŚĆ NA ROZCIĄGANIE
Bardziej szczegółowoKrytyczne czynniki sukcesu w zarządzaniu projektami
Seweryn SPAŁEK Krytyczne czynniki sukcesu w zarządzaniu projektami MONOGRAFIA Wydawnictwo Politechniki Śląskiej Gliwice 2004 SPIS TREŚCI WPROWADZENIE 5 1. ZARZĄDZANIE PROJEKTAMI W ORGANIZACJI 13 1.1. Zarządzanie
Bardziej szczegółowoWAVELET TRANSFORM OF SELECTED SIMULATION SIGNALS USING DETAILS AS INFORMATION SOURCE
TRANSPORT PROBLEMS 9 PROBLEMY TRANSPORTU Volume 4 Issue 3 Part Izabela JÓZEFCZYK Warsaw University of Technology, Engineering, Mechanics and Petrochemistry Department, Technical and Social Science School
Bardziej szczegółowoWPŁYW SZYBKOŚCI STYGNIĘCIA NA WŁASNOŚCI TERMOFIZYCZNE STALIWA W STANIE STAŁYM
2/1 Archives of Foundry, Year 200, Volume, 1 Archiwum Odlewnictwa, Rok 200, Rocznik, Nr 1 PAN Katowice PL ISSN 1642-308 WPŁYW SZYBKOŚCI STYGNIĘCIA NA WŁASNOŚCI TERMOFIZYCZNE STALIWA W STANIE STAŁYM D.
Bardziej szczegółowoDiscretization of continuous signals (M 19) Dyskretyzacja sygnałów ciągłych
SILESIAN UNIVESITY OF TECHNOLOGY FACULTY OF ENERGY AND ENVIRONMENTAL ENGINEERING INSTITUTE OF POWER ENGINEERING AND TURBOMACHINERY POLITECHNIKA ŚLĄSKA WYDZIAŁ INŻYNIERII ŚRODOWISKA I ENERGETYKI INSTYTUT
Bardziej szczegółowoŁukasz Reszka Wiceprezes Zarządu
Łukasz Reszka Wiceprezes Zarządu Time for changes! Vocational activisation young unemployed people aged 15 to 24 Projekt location Ząbkowice Śląskie project produced in cooperation with Poviat Labour Office
Bardziej szczegółowoSHP / SHP-T Standard and Basic PLUS
Range Features ErP compliant High Pressure Sodium Lamps Long life between 24,000 to 28,000 hours, T90 at 16,000 hours Strong performance with high reliability Car park, Street and Floodlighting applications
Bardziej szczegółowoAllocation of elements in former farmland afforestation with birch of varying age
Allocation of elements in former farmland afforestation with birch of varying age Gawęda Tomasz 1, Małek Stanisław 2 Michał Zasada 3 1 Nadleśnictwo Bielsko, RDLP Katowice 2 Department of Forest Ecology,
Bardziej szczegółowoA R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume Issue 3 DOI: /v
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 56 2011 Issue 3 DOI: 10.2478/v10172-011-0081-1 B. NIŻNIK, M. PIETRZYK MODEL OF PHASE TRANSFORMATION FOR NIOBIUM MICROALLOYED STEELS
Bardziej szczegółowoPowerFlow Sundial: 7 $ 0 & Avanc Compatible 8 & - & & 9 & -. ,! " #$%& ' ()$%& * & +, - <.! + . / & = & ! / - 4.
PowerFlow Sundial: Avanc Compatible,,. Tel: 01, @, www..com Introduction PowerFlo Main Switch Sundial M 1 2 www.powerflowenergy.com Sundial ilithium Phosphate www.powerflowenergy.com Sundial M 1 2 3 7
Bardziej szczegółowoAN EFFECT OF FLOW NON-UNIFORMITY IN EARTH-TO-AIR MULTI-PIPE HEAT EXCHANGERS (EAHEs) ON THEIR THERMAL PERFORMANCE
Łukasz AMANOWICZ *, Janusz WOJTKOWIAK * Ground earth-to-air multi-pipe heat exchanger, flow rate non-uniformity, thermal performance AN EFFECT OF FLOW NON-UNIFORMITY IN EARTH-TO-AIR MULTI-PIPE HEAT EXCHANGERS
Bardziej szczegółowoZMIANY KINETYKI UTLENIANIA STALIWA Cr-Ni MODYFIKOWANEGO TYTANEM I CYRKONEM
77/18 ARCHIWUM ODLEWNICTWA Rok 2006, Rocznik 6, Nr 18 (1/2) ARCHIVES OF FOUNDRY Year 2006, Volume 6, N o 18 (1/2) PAN Katowice PL ISSN 1642-5308 ZMIANY KINETYKI UTLENIANIA STALIWA Cr-Ni MODYFIKOWANEGO
Bardziej szczegółowoHelena Boguta, klasa 8W, rok szkolny 2018/2019
Poniższy zbiór zadań został wykonany w ramach projektu Mazowiecki program stypendialny dla uczniów szczególnie uzdolnionych - najlepsza inwestycja w człowieka w roku szkolnym 2018/2019. Składają się na
Bardziej szczegółowoOBWIESZCZENIE MINISTRA INFRASTRUKTURY. z dnia 18 kwietnia 2005 r.
OBWIESZCZENIE MINISTRA INFRASTRUKTURY z dnia 18 kwietnia 2005 r. w sprawie wejścia w życie umowy wielostronnej M 163 zawartej na podstawie Umowy europejskiej dotyczącej międzynarodowego przewozu drogowego
Bardziej szczegółowoOCENA WPŁYWU TEMPERATURY CHŁODZENIA NA WYTRZYMAŁOŚĆ KINETYCZNĄ GRANUL
Inżynieria Rolnicza 6(94)/2007 OCENA WPŁYWU TEMPERATURY CHŁODZENIA NA WYTRZYMAŁOŚĆ KINETYCZNĄ GRANUL Marek Rynkiewicz Zakład Użytkowania Maszyn i Urządzeń Rolniczych, Akademia Rolnicza w Szczecinie Streszczenie.
Bardziej szczegółowoNo matter how much you have, it matters how much you need
CSR STRATEGY KANCELARIA FINANSOWA TRITUM GROUP SP. Z O.O. No matter how much you have, it matters how much you need Kancelaria Finansowa Tritum Group Sp. z o.o. was established in 2007 we build trust among
Bardziej szczegółowoInstrukcja obsługi User s manual
Instrukcja obsługi User s manual Konfigurator Lanberg Lanberg Configurator E-mail: support@lanberg.pl support@lanberg.eu www.lanberg.pl www.lanberg.eu Lanberg 2015-2018 WERSJA VERSION: 2018/11 Instrukcja
Bardziej szczegółowoEksperymenty reaktorowe drugiej generacji wyznaczenie ϑ 13
Eksperymenty reaktorowe drugiej generacji wyznaczenie ϑ 13 v Przypomnienie wyniku eksperymentu KamLAND - weryfikującego oscylacje neutrin słonecznych v Formuły na prawdopodobieństwo disappearance antyneutrin
Bardziej szczegółowoMikrostruktura, struktura magnetyczna oraz właściwości magnetyczne amorficznych i częściowo skrystalizowanych stopów Fe, Co i Ni
mgr inż. Jakub Rzącki Praca doktorska p.t.: Mikrostruktura, struktura magnetyczna oraz właściwości magnetyczne amorficznych i częściowo skrystalizowanych stopów Fe, Co i Ni STRESZCZENIE W pracy przedstawiono
Bardziej szczegółowoA R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 56 2011 Issue 3 DOI: 10.2478/v10172-011-0063-3
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 56 2011 Issue 3 DOI: 10.2478/v10172-011-0063-3 K. SOŁEK, M. KOROLCZUK-HEJNAK, M. KARBOWNICZEK AN ANALYSIS OF STEEL VISCOSITY IN THE
Bardziej szczegółowoInżynieria materiałowa: wykorzystywanie praw termodynamiki a czasem... walka z termodynamiką
Inżynieria materiałowa: wykorzystywanie praw termodynamiki a czasem... walka z termodynamiką Kilka definicji Faza Stan materii jednorodny wewnętrznie, nie tylko pod względem składu chemicznego, ale również
Bardziej szczegółowoMacromolecular Chemistry
Macromolecular Chemistry Mn = MiNi Ni Mw = WiMi = Wi NiMi 2 NiMi PI = M M w n Lecture 6 Molecular Weight Distribution in Polymeric Materials Polymer% Molecular weight adical Chain Growth Polymerization
Bardziej szczegółowoPrzewody do linii napowietrznych Przewody z drutów okrągłych skręconych współosiowo
POPRAWKA do POLSKIEJ NORMY ICS 29.060.10 PNEN 50182:2002/AC Wprowadza EN 50182:2001/AC:2013, IDT Przewody do linii napowietrznych Przewody z drutów okrągłych skręconych współosiowo Poprawka do Normy Europejskiej
Bardziej szczegółowoCFD MODELING OF PULVERIZED COAL COMBUSTION IN AIR AND OXY ATMOSPHERE - NO x AND SO 2 FORMATION
Proceedings of ECOpole DOI: 10.2429/proc.2013.7(1)019 2013;7(1) Halina PAWLAK-KRUCZEK 1 and Maciej ZAWIŚLAK 2 CFD MODELING OF PULVERIZED COAL COMBUSTION IN AIR AND OXY ATMOSPHERE - NO x AND SO 2 FORMATION
Bardziej szczegółowoWPŁYW WYBRANYCH CZYNNIKÓW TECHNOLOGICZNYCH NA STOPIEŃ ZAGAZOWANIA SILUMINÓW
15/10 Archives of Foundry, Year 2003, Volume 3, 10 Archiwum Odlewnictwa, Rok 2003, Rocznik 3, Nr 10 PAN Katowice PL ISSN 1642-5308 WPŁYW WYBRANYCH CZYNNIKÓW TECHNOLOGICZNYCH NA STOPIEŃ ZAGAZOWANIA SILUMINÓW
Bardziej szczegółowoROZPRAWY NR 128. Stanis³aw Mroziñski
UNIWERSYTET TECHNOLOGICZNO-PRZYRODNICZY IM. JANA I JÊDRZEJA ŒNIADECKICH W BYDGOSZCZY ROZPRAWY NR 128 Stanis³aw Mroziñski STABILIZACJA W ASNOŒCI CYKLICZNYCH METALI I JEJ WP YW NA TRWA OŒÆ ZMÊCZENIOW BYDGOSZCZ
Bardziej szczegółowoWalyeldeen Godah Małgorzata Szelachowska Jan Kryński. Instytut Geodezji i Kartografii (IGiK), Warszawa Centrum Geodezji i Geodynamiki
Porównanie globalnych modeli geopotencjału opracowanych na podstawie danych z misji GRACE oraz GOCE/GRACE z przyspieszeniem siły ciężkości pomierzonym w Obserwatorium Geodezyjno-Geofizycznym Borowa Góra
Bardziej szczegółowoTyp VFR. Circular flow adjustment dampers for the adjustment of volume flow rates and pressures in supply air and extract air systems
Typ VFR FOR THE RELIABLE BALANCING OF VOLUME FLOW RATES Circular flow adjustment dampers for the adjustment of volume flow rates and pressures in supply air and extract air systems Each flow adjustment
Bardziej szczegółowoANALIZA PARAMETRÓW DYNAMICZNYCH PULSATORÓW W WARUNKACH SYMULOWANEGO DOJU MECHANICZNEGO
Inżynieria Rolnicza 5(103)/2008 ANALIZA PARAMETRÓW DYNAMICZNYCH PULSATORÓW W WARUNKACH SYMULOWANEGO DOJU MECHANICZNEGO Adam Luberański, Magdalena Sopkowicz Instytut Inżynierii Rolniczej, Uniwersytet Przyrodniczy
Bardziej szczegółowoA R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume Issue 1 DOI: /amm
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 59 2014 Issue 1 DOI: 10.2478/amm-2014-0056 T. KNYCH, M. PIWOWARSKA-ULIASZ, P. ULIASZ ALUMINIUM ALLOYS WITH ZIRCONIUM ADDITIONS, IN
Bardziej szczegółowoLaboratory Studies on the Effectiveness of NO x Reduction by Selective Catalytic Reduction SCR Method
MIDDLE POMERANIAN SCIENTIFIC SOCIETY OF THE ENVIRONMENT PROTECTION ŚRODKOWO-POMORSKIE TOWARZYSTWO NAUKOWE OCHRONY ŚRODOWISKA Annual Set The Environment Protection Rocznik Ochrona Środowiska Volume/Tom
Bardziej szczegółowoSTRUCTURE OF PHOSPHOR TIN BRONZE CuSn10P MODIFIED WITH MIXTURE OF MICROADDITIVES
11/15 Archives of Foundry, Year 2005, Volume 5, 15 Archiwum Odlewnictwa, Rok 2005, Rocznik 5, Nr 15 PAN Katowice PL ISSN 1642-5308 STRUCTURE OF PHOSPHOR TIN BRONZE CuSn10P MODIFIED WITH MIXTURE OF MICROADDITIVES
Bardziej szczegółowophoto graphic Jan Witkowski Project for exhibition compositions typography colors : +48 506 780 943 : janwi@janwi.com
Jan Witkowski : +48 506 780 943 : janwi@janwi.com Project for exhibition photo graphic compositions typography colors Berlin London Paris Barcelona Vienna Prague Krakow Zakopane Jan Witkowski ARTIST FROM
Bardziej szczegółowoOKREŚLANIE ZALEŻNOŚCI POMIĘDZY CZASEM KRYSTALIZACJI EUTEKTYCZNEJ A ZABIELANIEM ŻELIWA. Z. JURA 1 Katedra Mechaniki Teoretycznej Politechniki Śląskiej
20/44 Solidification of Metals and Alloys, Year 2000, Volume 2, Book No. 44 Krzepnięcie Metali i Stopów, Rok 2000, Rocznik 2, Nr 44 PAN Katowice PL ISSN 0208-9386 OKREŚLANIE ZALEŻNOŚCI POMIĘDZY CZASEM
Bardziej szczegółowoLatent Dirichlet Allocation Models and their Evaluation IT for Practice 2016
Latent Dirichlet Allocation Models and their Evaluation IT for Practice 2016 Paweł Lula Cracow University of Economics, Poland pawel.lula@uek.krakow.pl Latent Dirichlet Allocation (LDA) Documents Latent
Bardziej szczegółowoZadanie ChemCad - Batch Reaktor
Zadanie ChemCad - Batch Reaktor Opracowanie: dr inŝ. E.Wolak Treść zadania: Octan sodu powstaje w wyniku reakcji: NaOH + C2 H5COOCH3 C2H5OH + CH3COONa Wodorotlenek sodu i octan etylu zasilają reaktor okresowy
Bardziej szczegółowoASSESSMENT OF IMPACT OF THE RHEOLOGICAL PARAMETERS CHANGE ON SENSITIVITY OF THE ASPHALT STRAIN BASED ON THE TEST RESULTS
CIVIL AND ENVIRONMENTAL ENGINEERING REPORTS ISSN 2080-5187 CEER 2015; 16 (1): 105-117 DOI: 10.1515/ceer-2015-0008 ASSESSMENT OF IMPACT OF THE RHEOLOGICAL PARAMETERS CHANGE ON SENSITIVITY OF THE ASPHALT
Bardziej szczegółowoSEZONOWE ZMIANY STOPNIA ZAPYLENIA ATMOSFERY W REJONIE UPRZEMYSŁOWIONYM NA PODSTAWIE OBSERWACJI WIELOLETNICH
SEZONOWE ZMIANY STOPNIA ZAPYLENIA ATMOSFERY W REJONIE UPRZEMYSŁOWIONYM NA PODSTAWIE OBSERWACJI WIELOLETNICH TARCZYŃSKI Lesław Wydział Budownictwa, Politechnika Opolska SEASONAL FLUCTUATIONS OF THE ATMOSPHERE
Bardziej szczegółowoStreszczenie rozprawy doktorskiej
Doskonalenie pomiaru zawartości wody w produktach spożywczych z wykorzystaniem metody wagosuszarkowej bazującej na promieniowaniu IR mgr Sławomir Janas Streszczenie rozprawy doktorskiej Promotor pracy:
Bardziej szczegółowoSTRUKTURA ŻELIWA EN-GJS W ZALEŻNOŚCI OD MATERIAŁÓW WSADOWYCH
3/22 Archives of Foundry, Year 2006, Volume 6, 22 Archiwum Odlewnictwa, Rok 2006, Rocznik 6, Nr 22 PAN Katowice PL ISSN 1642-5308 STRUKTURA ŻELIWA EN-GJS-500-7 W ZALEŻNOŚCI OD MATERIAŁÓW WSADOWYCH D. BARTOCHA
Bardziej szczegółowoInstitute of Metallurgy and Materials Science, Polish Academy of Sciences: metallurgist (since 2010), assistant professor (since 2014).
Phone: (012) 295 28 12; (012) 295 28 22 (lab.); fax: (012) 295 28 04 email: h.kazimierczak@imim.pl Employment and positions Institute of Metallurgy and Materials Science, Polish Academy of Sciences: metallurgist
Bardziej szczegółowoATMOSFERA TOPIENIA W ODLEWNICZYCH PROCESACH PRZETAPIANIA STOPÓW MIEDZI CZĘŚĆ III
10/9 Archives of Foundry, Year 2003, Volume 3, 9 Archiwum Odlewnictwa, Rok 2003, Rocznik 3, Nr 9 PAN Katowice PL ISSN 1642-5308 ATMOSFERA TOPIENIA W ODLEWNICZYCH PROCESACH PRZETAPIANIA STOPÓW MIEDZI CZĘŚĆ
Bardziej szczegółowo